Contact: Jiang Yu Qin Tel: 186697353078 HGM a seat by a high-strength cement slurry material, a variety of complex additives and selected by a special process aggregate formulated with high fluidity, no shrinkage, early strength and high strength and other characteristics of a base paste a ★ ??Uses for a variety of mechanical and electrical equipment (heavy equipment, high-precision grinding machines) and the seat of a grout slurry pier production. ★ Specifications Item Index compressive strength (MPa) ≥ 3 天 天 ≥50 ≥30 28 degrees extension (mm) ≥200 expansion (one day)% ≥0.020 bleeding rate% 0 ★ construction points (a) basic processing and formwork: 1 basis chiseling concrete surface, and clean up. Pulp and seat components bonded together (eg steel plate) will rust and oil and other skin removed. 2, Block 4 hours before watering slurry on the surface of the concrete foundation is applied to wet, do not have water when watering. 3, the baffle should support set tight to prevent leakage of plasma. (B) the filling: 1, add water: According bag (25kg) ratio of 4.0 ~ 4.5kg of water mixing with water, such as the construction does not require a large degree can be a corresponding reduction in the flow of water. 2, mixing procedure: After mixing bucket predetermined amount of water is added into blender, a part of the seat into the barrel stirred dilute slurry, then I feed into the mixing time should be controlled from start to finish in one minute about. 3, stirring blades should move slowly up and down along the periphery of the barrel to make the bottom of the barrel and the barrel wall adhesion of dry material to be mixing; mixing blades must not be raised to the top of the seat into the seat to avoid air slurry liquid slurry 4, mixing good seat clay slurry should be watered. When watering, as far as possible from the side of the injection, in order to facilitate the discharge of air between the floor and the concrete foundation. When necessary, can be used bamboo and other tools diversion. Watering must be continuous after the start, without interruption. ★ ① double handle mixer with hand drill, power ≥450W, speed ≥500r / min. ② mixing blades made of δ = 1.2mm thick steel blade φ150mm, stirring rod φ12mm round. ★ Note the use of the site is strictly prohibited incorporate any admixtures, admixture in cement. Not with other manufacturers of similar products mix, in order to ensure project quality. ★ conservation 1, with wet straw bags or cloth seat cover slurry has been poured on the good, and sprinkler maintenance, 2-6 times a day. 2, the curing temperature should be above 15 ℃, curing period of 7 days. Maintenance period may be extended if the field temperature is lower. 3, winter construction insulation measures need to be taken. ★ Chaimo form removal should be watered after the completion of 24 hours after form removal continued maintenance. ★ Packaging and storage Packing for 25kg ± 0.5kg, composite paper bag lined with plastic bag. Store in a dry, cool place, without the moisture stored at the storage period of three months. Overdue need re-examination, after passing before use ★ Ridge Zhangjiakou Power Plant project performance, the Ming Tombs Pumped Storage Power Station, the Three Gorges Project, Henan Jiaozuo Power Plant, Henan First Thermal Power Construction Company, Beijing People's Hospital, SOHU district, West Central Square, Shunyi Korean barbecue city, Fenghui era, TEDA Xintiandi Monte, new industry and so on Laguna Beach.